321 سټینلیس سټیل پټه
د سټینلیس سټیل شیټ پلیټ درجې Baogu عرضه
| ډول | درجه | درجه | د کیمیاوي برخې٪ | ||||||||||
| C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | نور | |||
| آستینیتیک | ۲۰۱ | SUS201 | ≤0.15 | 16.00-18.00 | 3.50-5.50 | 5.50-7.50 | ≤0.060 | ≤0.030 | - | ≤1.00 | - | ≤0.25 | - |
| ۲۰۲ | SUS202 | ≤0.15 | 17.00-19.00 | 4.00-6.00 | 7.50-10.00 | ≤0.060 | ≤0.030 | ≤1.00 | - | ≤0.25 | - | ||
| ۳۰۱ | 1.431 | ≤0.15 | 16.00-18.00 | 6.00-8.00 | ≤ 2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | ≤0.10 | - | |
| ۳۰۴ | 1.4301 | ≤0.07 | 17.00-19.00 | 8.00-10.00 | ≤ 2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 304L | 1.4307 | ≤0.030 | 18.00-20.00 | 8.00-10.00 | ≤ 2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 304H | 1.4948 | 0.04-0.10 | 18.00-20.00 | 8.00-10.00 | ≤ 2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| ۳۰۹ | 1.4828 | ≤0.20 | 22.00-24.00 | 12.00-15.00 | ≤ 2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 309S | * | ≤0.08 | 22.00-24.00 | 12.00-15.00 | ≤ 2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | - | |
| ۳۱۰ | 1.4842 | ≤0.25 | 24.00-26.00 | 19.00-22.00 | ≤ 2.00 | ≤0.045 | ≤0.030 | - | ≤1.50 | - | - | - | |
| 310S | * | ≤0.08 | 24.00-26.00 | 19.00-22.00 | ≤ 2.00 | ≤0.045 | ≤0.030 | - | ≤1.50 | - | - | - | |
| ۳۱۴ | 1.4841 | ≤0.25 | 23.00-26.00 | 19.00-22.00 | ≤ 2.00 | ≤0.045 | ≤0.030 | - | 1.50-3.00 | - | - | - | |
| ۳۱۶ | 1.4401 | ≤0.08 | 16.00-18.50 | 10.00-14.00 | ≤ 2.00 | ≤0.045 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | - | - | |
| 316L | 1.4404 | ≤0.030 | 16.00-18.00 | 10.00-14.00 | ≤ 2.00 | ≤0.045 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | - | - | |
| 316Ti | 1.4571 | ≤0.08 | 16.00-18.00 | 10.00-14.00 | ≤ 2.00 | ≤0.045 | ≤0.030 | 2.00-3.00 | ≤1.00 | - | 0.1 | Ti5(C+N)~0.70 | |
| ۳۱۷ | * | ≤0.08 | 18.00-20.00 | 11.00-15.00 | ≤ 2.00 | ≤0.045 | ≤0.030 | 3.00-4.00 | ≤1.00 | - | 0.1 | - | |
| 317L | 1.4438 | ≤0.03 | 18.00-20.00 | 11.00-15.00 | ≤ 2.00 | ≤0.045 | ≤0.030 | 3.00-4.00 | ≤1.00 | - | 0.1 | - | |
| ۳۲۱ | 1.4541 | ≤0.08 | 17.00-19.00 | 9:00-12:00 | ≤ 2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | Ti5(C+N)~0.70 | |
| ۳۲۱هـ | * | 0.04-0.10 | 17.00-19.00 | 9:00-12:00 | ≤ 2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | Ti5(C+N)~0.70 | |
| ۳۴۷ | 1.455 | ≤0.08 | 17.00-19.00 | 9:00-12:00 | ≤ 2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | Nb≥10*C%-1.10 | |
| ۳۴۷هـ | 1.494 | 0.04-0.10 | 17.00-19.00 | 9:00-12:00 | ≤ 2.00 | ≤0.045 | ≤0.030 | - | ≤1.00 | - | - | Nb≥10*C%-1.10 | |
| xm-19 | نايټرونيك 50 | ≤0.06 | 20.50-23.50 | 11.50-13.50 | 4.0-6.0 | ≤0.045 | ≤0.030 | 1.50-3.00 | ≤1.00 | - | 0.2-0.4 | نوټ: 0.10-0.30 V: 0.10-0.30 | |
| 904L | N08904 | ≤0.02 | 19.0-23.0 | 23.0-28.0 | 4.0-5.0 | ≤0.045 | ≤0.035 | ≤1.00 | 0.1 | Cu: 1.0-2.0 | |||
| دوه مخی | ۲۲۰۵ | S32205 | ≤0.03 | 22.0-23.0 | 4.5-6.5 | ≤ 2.00 | ≤0.030 | ≤0.020 | 3.0-3.5 | ≤1.00 | - | 0.14-0.20 | |
| 2507 | S32750 | ≤0.03 | 24.0-26.0 | 6.0-8.0 | ≤1.20 | ≤0.035 | ≤0.020 | 3.0-5.0 | ≤0.80 | 0.5 | 0.24-0.32 | ||
| * | S32760 | ≤0.03 | 24.0-26.0 | 6.0-8.0 | ≤1.00 | ≤0.030 | ≤0.010 | 3.0-4.0 | ≤1.00 | 0.5-1.00 | 0.2-0.3 | ||
| ۲۳۰۴ | S32304 | ≤0.03 | 21.5-24.5 | 3.0-5.5 | ≤ 2.50 | ≤0.040 | ≤0.030 | 0.05-0.6 | ≤1.00 | 0.05-0.6 | 0.05-0.2 | ||
| ۳۲۹ | 1.446 | ≤0.08 | 23.00-28.00 | 2.00-5.00 | ≤1.00 | ≤0.040 | ≤0.030 | 1.00-2.00 | ≤0.75 | - | - | ||
| فیرایټ | 409 | S40900 | ≤0.03 | 10.50-11.70 | 0.5 | ≤1.00 | ≤0.040 | ≤0.020 | - | ≤1.00 | - | ≤0.030 | Ti6(C+N)~0.50 Nb:0.17 |
| ۴۳۰ | 1Cr17 | ≤0.12 | 16.00-18.00 | - | ≤1.0 | ≤0.040 | ≤0.030 | - | ≤1.0 | - | - | - | |
| ۴۴۴ | S44400 | ≤0.025 | 17.50-19.50 | 1 | ≤1.00 | ≤0.040 | ≤0.030 | 1.75-2.5 | ≤1.00 | - | 0.035 | Ti+Nb:0.2+4(C+N)~0.80 | |
| ۴۴۶ | S44600 | ≤0.20 | 23.00-27.00 | 0.75 | ≤1.5 | ≤0.040 | ≤0.030 | 1.50-2.50 | ≤1.00 | - | ≤0.25 | - | |
| مارټینسایټ | 410 | 1Cr13 | 0.08-0.15 | 11.50-13.50 | 0.75 | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤1.00 | - | - | - |
| 410S | * | ≤0.080 | 11.50-13.50 | 0.6 | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤1.00 | - | - | - | |
| ۴۱۶ | Y1Cr13 | ≤0.15 | 12.00-14.00 | 3) | ≤1.25 | ≤0.060 | ≥0.15 | - | ≤1.00 | - | - | - | |
| 420 | 2Cr13 | ≥0.15 | 12.00-14.00 | - | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤1.00 | - | - | - | |
| 420J2 | 3Cr13 | 0.26-0.35 | 12.00-14.00 | - | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤1.00 | - | - | - | |
| ۴۳۱ | 1Cr17Ni2 | ≤0.20 | 15.00-17.00 | 1.50-2.50 | ≤1.00 | ≤0.040 | ≤0.030 | - | ≤0.80 | - | - | - | |
| 440C | 11Cr17 | 0.95-1.20 | 16.00-18.00 | - | ≤1.00 | ≤0.040 | ≤0.030 | 0.75 | ≤1.00 | - | - | - | |
| PH | ۶۳۰ | 17-4PH | ≤0.07 | 15.00-17.50 | 3.00-5.00 | ≤1.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | 3.00-5.00 | - | Nb 0.15-0.45 |
| ۶۳۱ | 17-7PH | ≤0.09 | 16.00-18.00 | 6.50-7.50 | ≤1.00 | ≤0.035 | ≤0.030 | - | ≤1.00 | ≤0.50 | - | Al 0.75-1.50 | |
| ۶۳۲ | 15-5PH | ≤0.09 | 14.00-16.00 | 3.50-5.50 | ≤1.00 | ≤0.040 | ≤0.030 | 2.00-3.00 | ≤1.00 | 2.5-4.5 | - | Al 0.75-1.50 | |
تفصیل
د 321 سټینلیس سټیل پټه د آسټینټیک سټینلیس سټیل ډول دی چې د ټیټ کاربن مینځپانګې سره او د ډیری ککړ چاپیریال لپاره ښه سنکنرن مقاومت لري.321 د ښه ویلډ وړتیا، ښه ماشین وړتیا او د پام وړ جوړونې ملکیتونه وړاندې کوي.
د 321 سټینلیس سټیل پټه معمولا د کیمیاوي صنعت ، د نبض او کاغذ صنعت ، سمندري او ساحل انجینري صنعتونو او همدارنګه د خواړو او مشروباتو صنعتونو کې کارول کیږي.
د 321 سټینلیس سټیل پټه هم د کلورایډ فشار سنکنرن کریک کولو او پیټینګ لپاره د لوړې کچې مقاومت لري.دا د هایدروکلوریک اسید په وړاندې هم مقاومت لري تر 250 ° C (480 ° F) پورې په لوړه تودوخه کې.
برخی
د ښه سنکنرن مقاومت: د 321 سټینلیس سټیل پټه د 304 او 316 ډوله سټینلیس سټیلونو په پرتله غوره سنکنرن مقاومت لري ، کوم چې دا په سنګر چاپیریال کې د کارولو لپاره مثالی کوي.
عالي ویلډینګ وړتیا: د 321 سټینلیس سټیل پټه د ټولو میتودونو لخوا ویلډ کیدی شي پشمول د آرک ویلډینګ (TIG / GTAW) ، د الکترون بیم ویلډینګ (EBW / EFW) ، ډوب شوي آرک ویلډینګ (SAW) او لیزر بیم ویلډینګ (LBIW).
لوړ ځواک: د 321 سټینلیس سټیل پټې د ځواک کچه د 304 ډوله سټینلیس سټیلونو په پرتله 50٪ لوړه ده او د 316 ډول سټینلیس سټیلونو څخه تر 80٪ پورې لوړه ده د دوی د کاربن مینځپانګې او آسټینیټ غلو اندازې له امله.